Rubbery compounds as modifiers for poly(arylene sulfide)

ABSTRACT

A composition and method for forming the composition providing a molding composition of poly(arylene sulfide) and a crack resistance and/or an impact strength improving amount of a polymeric rubber chosen from among silicone rubber, ethylene-acrylic rubber, ethylene-propylene rubber, ethylene-propylene-diene rubber, and poly(butyl acrylate) rubber. In embodiments of the invention the improvement is enhanced by the addition of organosilane to the composition.

This application is a Division of application Ser. No. 552,884, now U.S. Pat. No. 4,581,411.

BACKGROUND OF THE INVENTION

This invention relates to compositions containing poly (arylene sulfide). In one of its aspects this invention relates to molding compositions containing poly(arylene sulfide). In another of its aspects this invention relates to a method for preparing compositions of poly(arylene sulfide) having improved impact strength and crack resistance.

Poly(arylene sulfide) is known to be useful as a molding composition. Among the characteristics of a molding composition that are important in determining the overall usefulness of the composition are the impact resistance or impact strength and the crack resistance. Molding compositions having good impact strength can be used in the molding of a great number of useful objects in which molding compositions that do not have good impact strength cannot be used because without good impact strength the molded objects tend to chip, crack or break when impacted with another object. Crack resistance is especially important in the molding of thick objects. It has now been found that the impact resistance and/or crack resistance of poly(arylene sulfide) can be improved by compounding with certain rubbery polymeric compounds. Using some of these rubbery compounds the impact strength can be further enhanced by the addition of cerain organic silanes.

It is therefore an object of this invention to provide a method for improving the impact strength and crack resistance of compositions containing poly(arylene sulfide), especially poly(phenylene sulfide). It is another object of this invention to provide compositions containing poly(arylene sulfide), especially poly(phenylene sulfide) which have improved impact strength and crack resistance. It is still another object of this invention to provide molded objects having improved impact strength and crack resistance.

Other aspects, objects and the various advantages of this invention will become apparent upon reading the specification and the appended claims.

STATEMENT OF THE INVENTION

According to this invention the impact strength and crack resistance of compositions containing poly(arylene sulfide) can be improved by the addition of an impact strength and crackc resistance improving amount of polymeric rubber chosen from among the group consisting of silicone rubber, ethylene-acrylic rubber, ethylene-propylene copolymer rubber, ethylene-propylene-diene terpolymer rubber, and poly(butyl acrylate) rubber.

In an embodiment of the invention a method is provided for improving the impact strength and crack resistance of a composition containing poly(phenylene sulfide) by admixing with a poly(phenylene sulfide) an impact strengh and crack resistance improving amount of a polymeric rubber chosen from among the group consisting essentially of silicone rubber, ethylene-acrylic rubber, ethylene-propylene copolymer rubber, ethylene-propylene-diene terpolymer rubber, and poly(butyl acrylate) rubber.

In embodiments of the invention the impact strength improvement is enhanced by the addition of an organosilane to the compositions containing poly(phenylene sulfide) and polymeric rubber.

The poly(phenylene sulfide) resins employed in the compositions are known polymers which have been set forth, for example, in U.S. Pat. No. 3,354,129 which issued November 21, 1967 to James T. Edmonds, Jr. and Harold Wayne Hill, Jr. The resins are normally solid materials which in an uncuredd or partially cured state can have melt flows in terms of g/10 minutes according to ASTM Method D-1238-70 (316° C. and 5 kg load) ranging from about 10 to about 10,000, more preferably from about 20 to about 3500. A presently preferred resin is poly(phenylene sulfide), abbreviated PPS.

The polymeric rubber used in the present invention is particularly effective for improving impact strength of poly(phenylene sulfide) when admixed therewith in amounts from about 0.1 to about 40 weight percent, preferably from about 0.5 to about 25 weight percent. The individual types of polymeric rubber can have a more preferred range of additive amount which will be discussed below.

The silicone rubber useful in the present invention can be described as a hydroxy-terminated diaryl silane/dialkyl silane copolymer. The silicone rubber additive is most preferably used in an amount of about 0.5 to about 10 weight percent in the composition.

The ethylene-acrylic rubber useful in the present invention can be described as a partially hydrolyzed ethylene-alkyl acrylate copolymer. The ethylene-acrylic rubber is most preferably used in an amount of about 0.5 to about 15 weight percent of the composition.

The ethylene-propylene rubber copolymer useful in this invention is most preferably used in an amount of about 0.5 to about 15 weight percent of the composition. Any rubbery ethylene-propylene copolymer is considered within the scope of this invention.

The ethylene-propylene-diene rubbery terpolymer is most preferably used in amount of about 0.5 to about 25 weight percent of the composition. Any ethylene-propylene-diene rubber terpolymer is considered within the scope of this invention.

The poly(butyl acrylate) rubber useful in the present invention can be describedd as a high molecular weight butyl acrylate-based rubber with hydroxy functionality. The poly(butyl acrylate) rubber is most preferably used in an amount of about 0.5 to about 25 weight percent of the composition.

When using either the silicone rubber or the poly(butyl acrylate) rubber it has been found that use of an organosilane in an amount of up to about 3 weight percent of the total composition, preferably about 0.1 to about 2 weight percent of the total composition, can further enhance the impact strength of the composition.

The organosilanes useful according to this invention can be described as alkyl or substituted alkyl trialkoxy silanes.

It is also within the scope of this invention that the compositions can contain other additives which can be chosen from reinforcing agents such as glass in the form of fibers or beads, fillers such as silica, clay, talc, calcium carbonate, and the like; processing aids such as lithium carbonate or oils or waxy compounds selected from among the N, N-alkylenebis (alkanamides), glyceride and phosphated glycerides of saturated fatty acids containing from 10 to 30 carbon atoms, mono- and di-alkanolamides derived from saturated faty acids and esters derived from a saturated long chain fatty acid and long chain saturated aliphatic alcohol; and colorants including carbon black, titanium dioxide, cadmium sulfide, cadmium sulfoselenide, phthalocyanine blue, iron oxide, and the like.

In the preparation of the compositions of this invention the order of addition is not important and any known means of mixing the components can be used, preferably dry ingredients can be tumble mixed and subsequently extruded and ground to form a homogeneous powder. The powder can then be reheated for molding.

The following examples will be used to describe the invention and should be taken as illustrative and not restrictive.

EXAMPLE 1

This example demonstrates the effectiveness of a silicone rubber on the impact resistance of a poly(p-phenylene sulfide) referred to hereinafter as PPS. The example also describes the general procedure for preparing and evaluating test specimens which is as follows: 900 grams of PPS (MR03, Phillips Petroleum Co., melt flow 20-65 grams per 10 minutes measured in accordance with test method ASTM D1238 at 600° F.(316° C. using a 5 kilogram weight) and 100 grams of a silicone rubber (PSW 1049, Petrarch Systems, Inc.) preground in a Wiley mill were mixed in a tumble mixer for about 5 minutes at ambient room temperature. The mixture was extruded through a Davis Standard extruder at 600° F. (316° C.), ground into a granular or coarse powder, dried in a 350° F. (177° C.) oven for 3 hours and molded into test specimens, 5 inches×1 inch×0.125 inch using a New Britain molding machine (barrel 600° F., mold 275° F.). Izod impact properties were then determined according to test method ASTM D 256 on notched and unnotched specimens.

Generally 4 tests were made and the results averaged. The procedure was repeated at various concenrations of silicone rubber and with two different types of organosilanes. The procedure was also repeated with a control, that is, with only the PPS and no additives. These results are listed in Table I showing that the addition of between 5 and 10 weight percent of the silicone rubber greatly increases both notched and unnotched impact resistance (Runs 2 and 3). The data also indicate that adding organosilane sometimes increases impact and sometimes decreases impact but generally only slightly either way.

                  TABLE I                                                          ______________________________________                                         Effect of Silicone Rubber                                                      on the lmpact Resistance of PPS                                                            PPS Compositions                                                               Run                                                                            1    2      3       4    5    6                                    ______________________________________                                         Components                                                                     PPS.sup.a     1000   950    900   950  900  900                                Silicone Rubber.sup.b                                                                        --     50     100   50   100  100                                Organosilane A.sup.c                                                                         --     --     --    1    2    --                                 Organosilane B.sup.d                                                                         --     --     --    --   --   2                                  Performance Property                                                           Annealed.sup.e                                                                 Impact Strength, J/M                                                           Notched       49     66     72    67   80   77                                 Unnotched     344    584    436   435  414  542                                ______________________________________                                          Notes:                                                                         .sup.a MR03, Phillips Petroleum Co.                                            .sup.b PSW 1049, Petrarch Systems, lnc. Base polymer is a 15% diphenyl         silane/85% dimethyl silane hydroxyterminated copolymer, mol. wt. approx.       600,000. To this base polymer was compounded 35 parts of a 325 m.sup.2 /g      surface area filler using 2 parts hexamethyldisilazane compounding aid. 1      Resin material (2 parts trimethylchlorosilane and 1 part                       ethylorthosilicate) was mixed into the rubber.                                 .sup.c A189, 3 mercaptopropyltrimethoxysilane, Union Carbide                   .sup.d A1100, 3 aminopropyltriethoxysilane, Union Carbide                      .sup.e Heated 185-195° C. for 2 to 4 hrs.                         

EXAMPLE II

This example demonstrates the effectiveness of any ethylene-acrylic rubber on the impact resistance of PPS. The proceddure described in Example I was repeated except the silicone elastomer was replaced with an ethylene-acrylic rubber, Vamac N-123. The results listed in Table II indicate the ethylene-acrylic rubber greatly increases impact resistance, particularly unannealed unnotched which was increased from 476 J/M to 1512 J/M.

                  TABLE II                                                         ______________________________________                                         Effect of Ethylene-Acrylic Rubber                                              on the Impact Resistance of PPS                                                                 PPS Composition                                                                Control                                                                               Invention                                              ______________________________________                                         Components, grams                                                              PPS.sup.a          1000     900                                                Ethylene-Acrylic rubber.sup.b                                                                     --       100                                                Performance Properties                                                         Annealed.sup.c                                                                 Impact Strength, J/M                                                           Notched            49       71                                                 Unnotched          344      614                                                Unannealed                                                                     Impact Strength, J/M                                                           Notched            41       78                                                 Unnotched          476      1512                                               ______________________________________                                          .sup.a See footnote a, Table I                                                 .sup.b Vamac N123, 100 parts of an ethylene/acrylic elastomer plus 23          parts fumed silica, DuPont                                                     .sup.c Heated 185-195° C. for 2 to 4 hrs.                         

EXAMPLE III

This example demonstrates the effectiveness of an ethylenepropylene rubbery copolymer (EPR) on impact resistance and crack resistance of PPS. In regards to impact resistance, the procedure described in Example I was again repeated except the silicone elastomer was replaced with an ethylene-propylene copolymer, EPsyn 7006. The results listed in Table III indicate the ethylene-propylene rubbery elastomer more than doubles and sometimes triples the impact resistance of PPS.

The effect of ethylene-propylene rubber on the crack resistance of a glass-filled PPS composition was determined by dry blending a composition comprised of 56.75 weight percent PPS (melt flow 173 from Phillips Petroleum Company), 40.00 weight percent fiberglass, 0.25 weight percent high density polyethylene (BX670 from Phillips Petroleum Company), 1.00 weight percent Li₂ CO₃, 2.00 weight percent iron oxide pigment (Davis Brown 6623), and then adding variable amounts of the ethylene-propylene polymer to be tested. The composition was extruded as described in Example I into disks 2 inches in diameter X 0.5 inch thick. After cooling to ambient room temperature the disks were further processed in one of two methods. In one method the disks were cut circumferentially to a thickness of 0.25 inch, annealed for 2 hours at 400° F., stored at ambient room temperature for 24 to 48 hours and visually examined for cracks. Eight such disks were prepared and a value of the number of disks exhibiting any degree of cracking recorded. In an alternate method, the reverse was carried out, namely, the disks were annealed first then cut, stored and examined for cracks. The results are recorded in Table IV and indicate that various type ethylene-propylene rubbers ranging in degree of ethylene content, M_(n) X10³, and Mooney value are satisfactory improving crack resistance of PPS compositions. The data also shows that the amount of rubber required for complete absence of cracking is about 2 weight percent but good cracking resistance is present even at 1 weight percent. PPS with varying melt flow as well as different composition ingredients and varying amounts will correspondingly alter the amount of ethylene-propylene rubber needed to provide satisfactory crack resistance.

                  TABLE III                                                        ______________________________________                                         Effect of Ethylene-Propylene Rubber                                            on the Impact Resistance of PPS                                                                   PPS Composition                                                                Control                                                                               Invention                                            ______________________________________                                         Components, grams                                                              PPS.sup.a            1000     900                                              Ethylene-Propylene copolymer.sup.b                                                                  --       100                                              Performance Properties                                                         Annealed.sup.c                                                                 Impact Strength, J/M                                                           Notched              49       104                                              Unnotched            344      1160                                             Unannealed                                                                     Impact strength, J/M                                                           Notched              41       114                                              Unnotched            476      1702                                             ______________________________________                                          .sup.a See footnote a, Table I                                                 .sup.b An ethylenepropylene copolymer, EPsyn 7006, 62-68 mole % ethylene,      M × 10.sup.3 = 50-60, Mooney viscosity 70(ML8 at 250F.), Copolymer       Rubber and Chem. Corp.                                                         .sup.c Heated 185-195° C. for 2 to 4 hrs.                         

                                      TABLE IV                                     __________________________________________________________________________     EFFECT OF ETHYLENE-PROPYLENE RUBBER ON THE CRACK                               RESISTANCE OF GLASS-FlLLED PPS                                                                 Wt. %                                                          Composition:    56.75                                                                              PPS.sup.a                                                                  40.00                                                                              Fiberglass                                                                 0.25                                                                               BX670 (High Density Poly-                                                      ethylene)                                                                  1.00                                                                               Li.sub.2 CO.sub.3                                                          2.00                                                                               Pigment                                                                    --  Ethylene-Propylene Rubber                                                             Cracks (No. of                                      Ethylene-Propylene Rubber  Disks Cracked                                                             Mooney                                                                              Out of 8 Tested).sup.f                                         Mole %     ML-8 at                                                                             Cut/-                                                                               Annealed/-                                     Trade Name                                                                            Wt. %                                                                              Ethylene                                                                            M.sub.n × 10.sup.3                                                             250° F.                                                                      Annealed                                                                            Cut                                            __________________________________________________________________________       None                                                                           (Control)                                                                           0   --         --   8    8                                                EPsyn                                                                          7006.sup.b                                                                          1   62-68                                                                               50-60 70   2    3                                                EPsyn                                                                          7006.sup.b                                                                          2   62-68                                                                               50-60 70   0    0                                                EPsyn                                                                          7006.sup.b                                                                          3   62-68                                                                               50-60 70   0    0                                                EPsyn                                                                          4006.sup.b                                                                          3   >68  40-50 40   2    0                                                Vistalon                                                                       719.sup.c                                                                           3   75   --    45-55.sup.e                                                                         0    0                                                Epcar                                                                          807.sup.d                                                                           3   70 ± 3                                                                           56    60 ± 6                                                                           0    0                                              __________________________________________________________________________      .sup.a Melt Flow 173 available from Phillips Petroleum Company.                .sup.b Available from Copolymer Rubber and Chemical Corporation.               .sup.c Available from Exxon Chemicals Americas.                                .sup.d Available from Polysar Incorp.                                          .sup.e ML1 at 260° F.                                                   .sup.f Sprue side of disks.                                              

EXAMPLE IV

This example demonstrates the effectiveness of a poly(butyl acrylate) rubber with and without the optional use of an organosilane on the impact resistance of PPS. The procedure described in Example I was once again repeated except the silicone elastomer was replaced with a poly(butyl acrylate) rubber, HYCAR 4004. The results listed in Table V show significant improvements in impact resistance of PPS particularly as the amount of poly(butyl acrylate) rubber is increased from 5% (Run 2) to 25% (Run 4). The data also indicates that organosilanes (1 weight %) enhance the butyl acrylate performance. It appears that when only a small amount of butyl acrylate rubber (5%) is added to the PPS other properties such as tensilel strength, flexural modulus and flexural strength are improved particularly when an organosilane is present (Compare Run 3 with 2 and 1). As the amount of butyl acrylate is increased to 25% these strength properties are decreased (Compare Run 3 with Runs 4, 5).

                  TABLE V                                                          ______________________________________                                         Effect of Poly(Butyl Acrylate) Rubber                                          on the Impact Resistance of PPS                                                             Run                                                                            1    2       3      4     5                                       ______________________________________                                         Components, grams                                                              PPS.sup.a      1000   950     950  750   750                                   Rubber.sup.b   --     50      50   250   250                                   Organosilane.sup.c -                                                                          --     --      10   --    10                                    Performance Properties.sup.d                                                   Annealed.sup.e                                                                 Flex. Modulus, MPa                                                                            3282   3146    3620 1864  1842                                  Flex. Strength, MPa                                                                           120    109     127  67    68                                    Ten. Strength, MPa                                                                            82     71      83   59    57                                    Impact Strength, J/M                                                           Notched        49     53      50   64    88                                    Unnotched      344    304     411  798   1097                                  Heat Distortion, °C.                                                                   110    108     108  102   102                                   Unannealed                                                                     Flex. Modulus, MPa                                                                            2814   2681    3094 1732  1663                                  Flex. Strength, MPa                                                                           105    91      105  47    51                                    Ten. Strength, MPa                                                                            60     52      72   47    49                                    Impact Strength, J/M                                                           Notched        41     51      44   74    111                                   Unnotched      476    351     427  824   1005                                  Heat Distortion, °C.                                                                   79     76      78   74    75                                    ______________________________________                                          .sup.a See footnote a, Table I?                                                .sup.b HYCAR 4004, high molecular weight polymer based on butyl acrylate       with hydroxy functionality from B. F. Goodrich                                 .sup.c A1100, 3aminopropyltriethoxysilane, Union Carbide                       .sup.d Run in accordance with test methods                                     Flex. Mod., Flex. St. ASTM D790                                                Ten. St. ASTM D636                                                             lzod lmpact ASTM D256                                                          Heat Distortion, °C. ASTM D648                                          .sup.e Heated 185-195° C. for 2 to 4 hrs.                         

EXAMPLE V

This example demonstrates the effectiveness of an ethylene-propylene-diene rubber (EPDM) on impact resistance and crack resistance of PPS. Both the impact resistance and crack resistance sample preparation and evaluations were carried out in the same manner as previously described. The results listed in table VI indicate the ethylene-propylene-diene rubbery elastomer significantly improves the impact resistance of PPS. Similarly the results listed in Table VII indicate the ethylene-propylene-diene rubbery elastomer generally eliminates all cracks in molded PPS compositions.

                  TABLE VI                                                         ______________________________________                                         EFFECT OF ETHYLENE-PROPYLENE-DIENE RUBBER                                      ON THE IMPACT RESISTANCE OF PPS                                                                    PPS Composition                                                                1     2                                                    ______________________________________                                         Composition: grams                                                             PPS.sup.a             1000    900                                              Ethylene-Propylene-Diene Rubber A.sup.b                                                              --      100                                              Performance Property:                                                          Annealed.sup.d                                                                 Impact Strength                                                                Notched               35      60                                               Unnotched             294     352                                              ______________________________________                                          .sup.2 See footnote Table I.                                                   .sup.b Ethylenepropylene-hexadiene rubbery polymer, Nordel 2722 available      from DuPont.                                                             

                  Table VII                                                        ______________________________________                                         EFFECT OF ETHYLENE-PROPYLENE-DlENE RUBBER                                      ON THE CRACK RESISTANCE OF PPS                                                           wt. %                                                                Composition:                                                                             55.10   PPS.sup.a                                                              38.84   Fiberglass                                                             0.24    BX670 (High Density Polyethylene)                                      0.97    Li.sub.2 SO.sub.3                                                      1.94    Pigment                                                                2.91    Ethylene-Propylene-Diene Rubber                                                  Cracks (No.                                                                    of Disks Cracked                                                               Out of 8 Tested).sup.d                                                         Cut/   Annealed/                                                               Annealed                                                                              Cut                                                 ______________________________________                                         1. None (Control)     8        8                                               2. Ethylene-Propylene-Diene Rubber A.sup.b                                                           0        0                                               3. Ethylene-Propylene-Diene Rubber B.sup.c                                                           1        0                                               ______________________________________                                          .sup.a PPS melt flow 173 from Phillips Petroleum Company.                      .sup.b Diene portion is ethylidenenorbornene with 5 double bonds per           molecule, Available from Copolymer Rubber and Chemical Corporation under       the tradename EPsyn 2506.                                                      .sup.c Diene portion is hexadiene, available from DuPont under the             tradename Nordel 2722.                                                         .sup.d Sprue side of disks.                                               

We claim:
 1. A molding composition comprising poly(arylene sulfide) and an impact strength and/or crack resistance improving amount of ethylene-propylene-diene rubber.
 2. A composition of claim 1 wherein the amount of ethylene-propylene-diene rubber is in a range of about 0.1 o about 40 weight percent of the composition.
 3. A composition of claim 2 wherein the amount of ethylene-propylene-diene rubber is in a range of about 0.5 to about 25 weight percent of the total composition. 